Condition |
Ultimate Tensile Strength |
0.2% Offset
Yield Strength |
Elongation |
Reduction of Area |
| ksi |
MPa |
ksi |
MPa |
% |
% |
| Solution Heat-treated |
108.0 |
745 |
49.0 |
338 |
48.5 |
69 |
| + 1200°F/8,000 h |
109.2 |
753 |
52.5 |
362 |
26.2 |
32.8 |
| + 1200°F/20,000 h |
112.4 |
775 |
53.5 |
369 |
24.2 |
34 |
| + 1200°F/30,000 h |
112.7 |
777 |
52.3 |
361 |
24.6 |
32.7 |
| + 1200°F/50,000 h |
113.0 |
779 |
53.1 |
366 |
23.2 |
32.5 |
|
| +1400°F/8,000 h |
101.8 |
702 |
47.9 |
330 |
18.2 |
17.6 |
| +1400°F/20,000 h |
101.2 |
698 |
43.3 |
299 |
18.0 |
17.2 |
| +1400°F/30,000 h |
101.5 |
700 |
44.8 |
309 |
19.7 |
18.4 |
| +1400°F/50,000 h |
99.8 |
688 |
44.9 |
310 |
14.8* |
10.8 |
|
| + 1600°F/8,000 h |
101.0 |
696 |
44.7 |
308 |
22.6 |
22.6 |
| + 1600°F/20,000 h |
96.9 |
668 |
40.9 |
282 |
19.4 |
17.9 |
| + 1600°F/30,000 h |
96.7 |
667 |
40.3 |
278 |
22.0 |
19.5 |
| + 1600°F/50,000 h |
94.3 |
650 |
39.8 |
274 |
20.1 |
18.2 |
*AGL, which tends to be lower; Other data are 4D Elong.