| Temperature | Creep, Percent | Average Initial Stress, Ksi (MPa)*
to Produce Specified Creep and Rupture |
| °F | °C | 10 Hours | 100 Hours | 1,000 Hours | 10,000 Hours |
|
| 1200 | 650 | 0.5 | 44.0 | (305) | 32.0 | (220) | 24.0 | (165) | - | - |
| | | 1.0 | 49.0 | (340) | 35.0 | (240) | 25.5 | (175) | 18.5 | (130) |
| | | Rupture | - | - | 53.0 | (365) | 38.0 | (260) | 27.5 | (190) |
|
| 1300 | 705 | 0.5 | 29.0 | (200) | 21.0 | (145) | 15.0 | (105) | - | - |
| | | 1.0 | 33.0 | (230) | 24.0 | (165) | 17.5 | (120) | 12.5 | (86) |
| | | Rupture | 52.0 | (360) | 37.0 | (255) | 26.0 | (180) | 17.0 | (115) |
|
| 1400 | 760 | 0.5 | 19.0 | (130) | 13.5 | (93) | 9.4 | (65) | - | - |
| | | 1.0 | 22.0 | (150) | 16.0 | (110) | 11.5 | (79) | 8.5 | (59) |
| | | Rupture | 35.0 | (240) | 25.0 | (170) | 17.5 | (120) | 11.9 | (82) |
|
| 1500 | 815 | 0.5 | 13.0 | (90) | 9.0 | (62) | 6.5 | (45) | - | - |
| | | 1.0 | 15.0 | (105) | 11.0 | (76) | 8.2 | (57) | 6.0 | (41) |
| | | Rupture | 25.0 | (170) | 17.0 | (115) | 11.8 | (81) | 7.6 | (52) |
|
| 1600 | 870 | 0.5 | 8.9 | (61) | 6.4 | (44) | 4.6 | (32) | - | - |
| | | 1.0 | 10.0 | (69) | 7.5 | (52) | 5.5 | (38) | 4.1 | (28) |
| | | Rupture | 17.0 | (115) | 11.5 | (79) | 7.5 | (52) | 4.9 | (34) |
|
| 1700 | 925 | 0.5 | 6.2 | (43) | 4.5 | (31) | 3.2 | (22) | - | - |
| | | 1.0 | 7.2 | (50) | 5.0 | (34) | 3.5 | (24) | 2.5 | (17) |
| | | Rupture | 12.0 | (83) | 7.6 | (52) | 4.8 | (33) | 3.0 | (21) |
|
| 1800 | 980 | 0.5 | 4.4 | (30) | 3.0 | (21) | 2.0 | (14) | - | - |
| | | 1.0 | 5.0 | (34) | 3.4 | (23) | 2.3 | (16) | 1.6 | (11) |
| | | Rupture | 7.5 | (52) | 4.8 | (33) | 3.0 | (21) | 1.9 | (13) |
Typical Creep and Stress Rupture Properties