Tensile Data

Short-Time Tensile Data

Form Condition Aging Test Temperature 0.2% Offset Yield Strength Ultimate Tensile Strength Elongation
Sheet 0.063 in. thick Heat-treated for at 2150°F (1177°C), RAC °F °C Time, h °F °C ksi MPa ksi MPa %
- - - RT RT 45.5 314 115.1 794 50.7
- - - 1100 593 32.9 227 86.9 599 45.3
- - - 1300 706 31.6 218 69.6 480 30.0
- - - 1500 816 29.5 203 55.9 385 24.3
- - - 1700 927 25.9 179 34.0 234 30.0
Aged 1500 816 128 RT RT 49.3 340 115.4 796 46.8
Heat-treated at 2150°F (1177°C), then welded andtested as-welded - - - RT RT - - 116.1 800 37.5
- - - 1200 649 - - 71.5 493 17.0
- - - 1300 704 - - 63.5 438 10.5
- - - 1500 816 - - 52.0 359 8.5
Sheet 0.045 in. thick Heat-treated at 2150°F (1177°C), then welded andtested as-welded, RAC - - - RT RT 44.7 308 114.4 789 50.0
- - - 1000 538 28.3 195 93.0 641 46.0
- - - 1100 593 28.9 199 93.0 641 50.0
- - - 1200 648 27.5 190 82.4 568 37.0
- - - 1300 704 28.0 193 69.9 482 24.0
- - - 1400 760 26.2 181 61.8 426 21.0
Aged 1000 538 10,000 RT RT 45.1 311 117.7 812 50.0
1100 593 10,000 RT RT 47.5 328 120.0 827 49.0
1200 648 10,000 RT RT 46.8 323 116.0 800 46.0
1300 704 10,000 RT RT 45.8 316 115.5 796 46.0
1400 760 10,000 RT RT 43.6 301 115.0 793 40.0
1000 538 10,000 1000 538 - - 97.7 674 46.0
1100 593 10,000 1100 593 - - 90.5 624 40.0
1200 648 10,000 1200 649 - - 81.9 565 32.0
1300 704 10,000 1300 704 - - 76.1 525 24.0
1400 760 10,000 1400 760 - - 65.1 449 20.0
Weld Metal As Welded - - RT RT - - 116.1 800 39.3*
- - 1200 649 - - 73.6 507 18.1*
Aged 1200 648 500 RT RT - - 116.8 805 38.6*
1200 648 500 1200 649 - - 82.7 570 26.5*

*Elongation in one inch
RT= Room Temperature

Hastelloy N alloy - Ultimate Tensile Strength & Elongation